Interface structure in a WC-Co alloy co-doped with VC and Cr3C2
Artikel i vetenskaplig tidskrift, 2012

The effect of carbide additions is investigated at the atom scale by studying the interface between the cubic carbide phase and the WC prismatic facet in a VC Cr 3 C 2 co-doped WC Co alloy using high-resolution transmission electron microscopy. The alloy was prepared from WC powder about 0.5 lm in size and sintered at 1400°C for 2 h. The orientation relationship between WC and the MC carbide at the prismatic facet of WC is the same orientation as the one found at a WC/(Cr, W)C interface in Cr 3 C 2 -doped alloys. the image of WC shows triangular patterns indicating the position of the C atomic columns in this crystal. In MC crystal, some elongation of the bright areas parallel to the interface is observed on the simulation. The presence of dislocations at interfaces can be related to the parametric mismatch between the two neighboring crystals, to the presence of different stable structural units, or to an angular deviation between the crystals.

cemented carbides

HREM

segregation

thin films

microscopy

interface structure

Författare

S. Lay

Institut polytechnique de Grenoble (Grenoble INP)

M. Loubradou

Institut polytechnique de Grenoble (Grenoble INP)

Sven Johansson

Chalmers, Teknisk fysik, Material- och ytteori

Göran Wahnström

Chalmers, Teknisk fysik, Material- och ytteori

Journal of Materials Science

0022-2461 (ISSN) 1573-4803 (eISSN)

Vol. 47 3 1588-1593

Styrkeområden

Nanovetenskap och nanoteknik

Materialvetenskap

Ämneskategorier

Materialteknik

Infrastruktur

C3SE (Chalmers Centre for Computational Science and Engineering)

DOI

10.1007/s10853-011-6156-6

Mer information

Senast uppdaterat

2021-11-24