Templated Growth of Covalently Bonded Three-Dimensional Carbon Nanotube Networks Originated from Graphene
Artikel i vetenskaplig tidskrift, 2012

A template-assisted method that enables the growth of covalently bonded three-dimensional carbon nanotubes (CNTs) originating from graphene at a large scale is demonstrated. Atomic force microscopy-based mechanical tests show that the covalently bonded CNT structure can effectively distribute external loading throughout the network to improve the mechanical strength of the material.

covalent bonding

switches

elastic properties

strength

transport

y-junctions

conductivity

mechanism

laser-ablation

membranes

carbon nanotube

arc-discharge method

templated growth

mechanical strength

graphene

Författare

Yifeng Fu

Chalmers, Teknisk fysik, Elektronikmaterial och system

Björn Carlberg

Chalmers, Teknisk fysik, Elektronikmaterial och system

Niklas Lindahl

Göteborgs universitet

Niclas Lindvall

Chalmers, Mikroteknologi och nanovetenskap (MC2), Kvantkomponentfysik

Johan Bielecki

Chalmers, Teknisk fysik, Kondenserade materiens fysik

Aleksandar Matic

Chalmers, Teknisk fysik, Kondenserade materiens fysik

Yuxin Song

Chalmers, Mikroteknologi och nanovetenskap (MC2), Fotonik

Zhili Hu

Chalmers, Teknisk fysik, Elektronikmaterial och system

Zonghe Lai

Chalmers, Mikroteknologi och nanovetenskap (MC2), Nanotekniklaboratoriet

L. Ye

SHT Smart High-Tech

Jie Sun

Chalmers, Mikroteknologi och nanovetenskap (MC2), Kvantkomponentfysik

Y. H. Zhang

Shanghai University

Y. Zhang

Shanghai University

Johan Liu

Chalmers, Teknisk fysik, Elektronikmaterial och system

Advanced Materials

0935-9648 (ISSN)

Vol. 24 12 1576-1581

Styrkeområden

Nanovetenskap och nanoteknik

Materialvetenskap

Ämneskategorier

Fysik

Infrastruktur

Nanotekniklaboratoriet

DOI

10.1002/adma.201104408

Mer information

Senast uppdaterat

2018-03-07