The influence of a KCl-rich environment on the corrosion attack of 304 L: 3D FIB/SEM and TEM investigations

Artikel i vetenskaplig tidskrift, 2021

This study investigates the intergranular corrosion of a stainless steel (304 L) in the presence of KCl(g)/KCl(s) at 600 ◦C by using a FIB/SEM to perform 3D reconstruction/tomography of grain boundary attacks in combination with TEM. The investigation shows that the combination of the 3D FIB/TEM offers a great potential for the study of complex features, i.e. intergranular corrosion. The initiation and propagation of the grain boundary attack occurred very rapidly below an intact secondary protection. No large accumulations of metal chlorides were observed at the grain boundary regions. Instead, indications of very rapid alloy diffusion in grain boundary regions were observed.