Tensile properties and microstructural characterization of Sn-0.7Cu-0.4Co bulk solder alloy for electronics applications
Artikel i vetenskaplig tidskrift, 2008

The ternary Sn–Cu–Co system eutectic composition was obtained by means of CALPHAD (CALculation of PHAse Diagram) methodology and it was found to be 0.4% Co and 0.7% Cu (wt%) with a melting point of 224 ◦C. The tensile behavior of this alloy was investigated at different strain rates (10−5, 10−4 and 10−3 s−1) and compared to both Sn–37Pb and Sn–4.0Ag–0.5Cu. The Sn–4.0Ag–0.5Cu alloy depicts the highest ultimate tensile strength (UTS) followed by the Sn–37P and finally the Sn–0.7Cu–0.4Co system. The elastic modulus was also higher for the Sn–4.0Ag–0.5Cu followed by the Sn–0.7Cu–0.4Co and last the Sn–37Pb. The microstructure of the Sn–0.7Cu–0.4Co alloy is composed of two types of intermetallic phases, (Cu,Co)6Sn5 and (Co,Cu)Sn2 dispersed in a Sn-rich matrix. The microstructure of this alloy proved to be very stable, after aging at 150 °C for 24 h. The eutectic Sn–0.7Cu–0.4Co solder alloy can therefore be a very good alternative for theSACalloys for surface mount technology applications.

Lead-free

Tensile properties

Strain rate

Solder alloy

Sn-Cu-Co

Författare

Cristina Andersson

Chalmers, Teknisk fysik, Elektronikmaterial

Peng Sun

Chalmers, Teknisk fysik, Elektronikmaterial

Johan Liu

Chalmers, Teknisk fysik, Elektronikmaterial

Journal of Alloys and Compounds

0925-8388 (ISSN)

Vol. 457 1/2 97-105

Ämneskategorier

Annan materialteknik

Annan elektroteknik och elektronik

DOI

10.1016/j.jallcom.2007.03.028

Mer information

Skapat

2017-10-07