Nanoparticles of the Lead-free Solder Alloy Sn-3.0Ag-0.5Cu with Large Melting Temperature Depression
Artikel i vetenskaplig tidskrift, 2009

Due to the toxicity of lead (Pb), Pb-containing solder alloys are being phased out from the electronics industry. This has lead to the development and implementation of lead-free solders. Being an environmentally compatible material, the lead-free Sn-3.0Ag-0.5Cu (wt.%) solder alloy is considered to be one of the most promising alternatives to replace the traditionally used Sn-Pb solders. This alloy composition possesses, however, some weaknesses, mainly as a result of its higher melting temperature compared with the Sn-Pb solders. A possible way to decrease the melting temperature of a solder alloy is to decrease the alloy particle size down to the nanometer range. The melting temperature of Sn-3.0Ag-0.5Cu lead-free solder alloy, both as bulk and nanoparticles, was investigated. The nanoparticles were manufactured using the self-developed consumable-electrode direct current arc (CDCA) technique. The melting temperature of the nanoparticles, with an average size of 30 nm, was found to be 213.9°C, which is approximately 10°C lower than that of the bulk alloy. The developed CDCA technique is therefore a promising method to manufacture nanometer-sized solder alloy particles with lower melting temperature compared with the bulk alloy.

Författare

Xiangdong Zou

Yulai Gao

Qijie Zhai

Cristina Andersson

Chalmers, Teknisk fysik, Elektronikmaterial

Johan Liu

Chalmers, Teknisk fysik, Elektronikmaterial

Journal of Electronic Materials

0361-5235 (ISSN) 1543-186X (eISSN)

Vol. 38 2 351-355

Ämneskategorier

Materialteknik

DOI

10.1007/s11664-008-0591-4

Mer information

Skapat

2017-10-07