Micro- and nano-patterned elastin-like polypeptide hydrogels for stem cell culture
Artikel i vetenskaplig tidskrift, 2017

We show that submicron-sized patterns can be imprinted into soft, recombinant-engineered protein hydrogels (here elastin-like proteins, ELP) by transferring wavy patterns from polydimethylsiloxane (PDMS) molds. The high-precision topographical tunability of the relatively stiff PDMS is translated to a bio-responsive, soft material, enabling topographical cell response studies at elastic moduli matching those of tissues. Aligned and unaligned wavy patterns with mold periodicities of 0.24–4.54 mm were imprinted and characterized by coherent anti-Stokes Raman scattering and atomic force microscopy. The pattern was successfully transferred down to 0.37 mm periodicity (width in ELP: 250 50 nm, height: 70 40 nm). The limit was set by inherent protein assemblies (diameter: 124–180 nm) that formed due to lower critical solution temperature behavior of the ELP during molding. The width/height of the ELP ridges depended on the degree of hydration; from complete dehydration to full hydration, ELP ridge width ranged from 79 9% to 150 40% of the mold width. The surface of the ridged ELP featured densely packed protein aggregates that were larger in size than those observed in bulk/flat ELP. Adipose-derived stem cells (ADSCs) oriented along hydrated aligned patterns with periodicities Z0.60 mm (height Z170 100 nm), while random orientation was observed for smaller distances/amplitudes, as well as flat and unaligned wavy ELP surfaces. Hence, micro-molding of ELP is a promising approach to create tissue-mimicking, hierarchical architectures composed of tunable micron-sized structures with nano-sized protein aggregates, which opens the way for orthogonal screening of cell responses to topography and cell-adhesion ligands at relevant elastic moduli.

Författare

Alexandra Paul

Chalmers, Biologi och bioteknik, Kemisk biologi

Michael Stührenberg

Chalmers, Fysik

Sharon Chen

Stanford University

Dongjoon Rhee

Northwestern University

Won-Kyu Lee

Northwestern University

Teri W. Odom

Northwestern University

S. C. Heilshorn

Stanford University

Annika Enejder

Chalmers, Biologi och bioteknik

Soft Matter

1744-683X (ISSN) 1744-6848 (eISSN)

Vol. 13 34 5665-5675

Ämneskategorier

Cellbiologi

DOI

10.1039/c7sm00487g

Mer information

Senast uppdaterat

2018-05-28