Modelling the Evolution of Multiple Hardening Mechanisms during Tempering of Fe-C-Mn-Ti Martensite
Artikel i vetenskaplig tidskrift, 2015

We model the hardness evolution of martensite during tempering as a linear addition of multiple hardening mechanisms that is combined with a microstructural Kampmann-Wagner-Numerical (KWN) model to simulate the nucleation and growth of TiC-precipitates during tempering. The combined model is fitted to the measured hardness evolution during tempering at 300 degrees C and 550 degrees C of martensitic steels with and without the addition of titanium. The model predicts TiC-precipitate sizes in agreement with experimental observations and generates fitting parameters in good agreement with literature. The microstructural components that give the highest contribution to the overall hardness are Fe3C precipitates (88 HV) and dislocations (54 HV). Both Fe3C- and dislocation-strengthening decreases rapidly during the initial stage and stabilise after 10 minutes of tempering. The model shows that the decrease in dislocation density due to recovery is slowed down due to the presence of TiC-precipitates. Titanium atoms in solid solution give a stable hardness contribution (25 HV) throughout the tempering process. TiC-precipitate strengthening generates a minor contribution (3.5 HV). The model shows that less than 1% of the equilibrium volume fraction of TiC-precipitates forms during isothermal tempering at 550 degrees C due to the large misfit strain (1.34 GJ/m(3)) and a limited density of potential nucleation sites in the martensite. The model shows that the hardness of tempered martensitic steels could potentially be increased by increasing the TiC-precipitate density by reducing the misfit strain.

microstructure

TiC

recovery

KWN-model

strengthening mechanism

martensite

Författare

Ceic Ohlund

Nedschroef Techno Centre

TU Delft

D. den Ouden

Materials Innovation Institute, Delft

TU Delft

Jonathan Weidow

Chalmers, Teknisk fysik, Materialens mikrostruktur

Mattias Thuvander

Chalmers, Teknisk fysik, Materialens mikrostruktur

S. E. Offerman

Chalmers, Teknisk fysik, Materialens mikrostruktur

ISIJ International

0915-1559 (ISSN)

Vol. 55 4 884-893

Ämneskategorier

Metallurgi och metalliska material

DOI

10.2355/isijinternational.55.884

Mer information

Senast uppdaterat

2021-09-21