As-Built and Post-treated Microstructures of an Electron Beam Melting (EBM) Produced Nickel-Based Superalloy
Artikel i vetenskaplig tidskrift, 2020

The microstructures of an electron beam melted (EBM) nickel-based superalloy (Alloy 718) were comprehensively investigated in as-built and post-treated conditions, with particular focus individually on the contour (outer periphery) and hatch (core) regions of the build. The hatch region exhibited columnar grains with strong 〈001〉 texture in the build direction, while the contour region had a mix of columnar and equiaxed grains, with no preferred crystallographic texture. Both regions exhibited nearly identical hardness and carbide content. However, the contour region showed a higher number density of fine carbides compared to the hatch. The as-built material was subjected to two distinct post-treatments: (1) hot isostatic pressing (HIP) and (2) HIP plus heat treatment (HIP + HT), with the latter carried out as a single cycle inside the HIP vessel. Both post-treatments resulted in nearly an order of magnitude decrease in defect content in hatch and contour regions. HIP + HT led to grain coarsening in the contour, but did not alter the microstructure in the hatch region. Different factors that may be responsible for grain growth, such as grain size, grain orientation, grain boundary curvature and secondary phase particles, are discussed. The differences in carbide sizes in the hatch and contour regions appeared to decrease after post-treatment. After HIP + HT, similar higher hardness was observed in both the hatch and contour regions compared to the as-built material.

Författare

Sneha Goel

Högskolan Väst

Hitesh Mehtani

Indian Institute of Technology Bombay

Shu Wei Yao

Xi'an Jiaotong University

Indradev Samajdar

Indian Institute of Technology Bombay

Uta Klement

Chalmers, Industri- och materialvetenskap, Material och tillverkning

S. Joshi

Högskolan Väst

Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

1073-5623 (ISSN)

Vol. 51 12 6546-6559

Ämneskategorier

Keramteknik

Metallurgi och metalliska material

Fusion, plasma och rymdfysik

DOI

10.1007/s11661-020-06037-z

Mer information

Senast uppdaterat

2020-11-30