Evidence for an unusual temperature dependence of the atmospheric corrosion of zinc
Artikel i vetenskaplig tidskrift, 2016

The atmospheric corrosion behavior of zinc in the presence of NaCl has been investigated using well-controlled laboratory exposures in 95% RH air at ten different temperatures in the range -4 to 22°C. Results show that a critical temperature (? -0.5°C) exists in zinc corrosion above which the rate of corrosion is constant/independent of temperature, and, below which there is a positive correlation between temperature and corrosion rate. The corrosion products formed above and below -0.5°C are also entirely different. While simonkolleite, hydrozincite and zinc carbonate hydroxide are the main corrosion products at T ?-0.5°C, the same compounds are absent at T < -0.5°C. Instead, sodium zinc carbonate (Na2Zn3(CO3)4.3H2O) is the dominant corrosion product at low temperature, together with Na2ZnCl4 · 3H2O and sweetite (Zn(OH)2). The results are interpreted in terms of two distinct corrosion modes prevailing at "high" and "low" temperature, respectively.

Författare

Mohsen Esmaily

Chalmers, Kemi och kemiteknik, Energi och material

Nooshin Mortazavi Seyedeh

Chalmers, Fysik, Materialens mikrostruktur

Jan-Erik Svensson

Chalmers, Kemi och kemiteknik, Energi och material

Lars-Gunnar Johansson

Chalmers, Kemi och kemiteknik, Energi och material

Journal of the Electrochemical Society

0013-4651 (ISSN) 1945-7111 (eISSN)

Vol. 163 14 C864-C872

Ämneskategorier

Kemi

DOI

10.1149/2.0751614jes

Mer information

Senast uppdaterat

2018-10-31