Surface characterization and electrochemical properties of hierarchically structured titanium surfaces
Journal article, 2013

Newly designed implant surfaces with hierarchic structure have been characterized with respect to chemical composition, topography, electrical properties and cell culturing. Three levels of surface roughness are induced starting from a blasted surface with the naturally formed oxide layer. Dissolution of the blasted surface is obtained by chemical treatment in oxalic acid. The surface becomes smoother with multitude of shallow depressions in the walls and bottoms of the blasted structure. The surface oxide layer formed is somewhat thicker than the naturally formed oxide and may contain oxalate. In the final step, part of the oxide layer is dissolved in hydrofluoric acid leading to a high concentration of soluble titanium species. A nanostructured surface is formed by precipitation of titanium oxide at spots on the surface where locally the pH is increased due to hydrogen evolution. The surface roughness is only marginally changed by the chemical treatment while the conductivity of the surface layer is lower for the chemically treated surfaces compared with the blasted reference. The hierarchical structure mimics many natural processes for achieving high shear strength.

xray diffraction


electron microscopy

electric properties



Ingela Mattisson

Christina Gretzer

Elisabet Ahlberg

University of Gothenburg

Materials Research Bulletin

Vol. 48 2 389-398

Subject Categories

Materials Chemistry



More information