Influence of pre-oxidation on dual atmosphere effect on AISI 441 interconnects for solid oxide fuel cell applications
Paper in proceedings, 2017

In previous studies an extreme dual atmosphere effect on the airfacing side of AISI 441 at 600°C was observed. However indications showed that pre-oxidation of the material might have a beneficial effect on the corrosion resistance in dual atmosphere. To examine this further we pre-oxidized AISI 441 samples for 0 min, 11 min, 45 min, 180 min and 280 min and subsequently exposed these at 600 °C for 500 h under dual atmosphere conditions. Photographs of the air-facing sides were taken throughout exposure to monitor the corrosion behavior. SEM analysis was performed on all samples after exposure.

Author

Claudia Goebel

Chalmers, Chemistry and Chemical Engineering, Energy and Material, Environmental Inorganic Chemistry

Patrik Alnegren

Chalmers, Chemistry and Chemical Engineering, Energy and Material, Environmental Inorganic Chemistry

Robin Faust

Chalmers, Chemistry and Chemical Engineering, Energy and Material, Environmental Inorganic Chemistry

Jan-Erik Svensson

Chalmers, Chemistry and Chemical Engineering, Energy and Material, Environmental Inorganic Chemistry

Jan Froitzheim

Chalmers, Chemistry and Chemical Engineering, Energy and Material, Environmental Inorganic Chemistry

ECS Transactions

1938-5862 (ISSN) 1938-6737 (eISSN)

Vol. 78 1 1559-1563

Infrastructure

Chalmers Materials Analysis Laboratory

Subject Categories

Corrosion Engineering

DOI

10.1149/07801.1559ecst

More information

Latest update

4/10/2019