Enhanced Fenton-Photocatalytic Degradation of Rhodamine B over Cobalt Ferrite Nanoparticles Synthesized by a Polyvinylpyrrolidone-Assisted Grinding Method

Journal article, 2024

A simple grinding method using polyvinylpyrrolidone (PVP) as a capping agent is introduced to synthesize CoFe2O4 nanoparticles. The effects of calcination temperature (ranging from 450 to 850 degrees C) on the structural, morphological, physical, and optical properties of the materials are investigated using various techniques, including thermogravimetric analysis/differential scanning calorimetry (TGA/DSC), powder X-ray diffraction (PXRD), transmission electron microscopy (TEM), N2 adsorption isotherm, ultraviolet-visible diffuse reflectance spectroscopy (UV-vis DRS), and vibrating sample magnetometry (VSM). The presence of PVP significantly suppresses the agglomeration of the materials, resulting in a nanocrystalline size of 18 nm for a sample calcined at 650 degrees C, which is approximately 38% smaller than that of the sample synthesized without PVP. Among the materials studied, the sample calcined at 650 degrees C exhibits unique properties, including optimal average pore size, specific surface area, and band gap energy, contributing to its superior photocatalytic degradation of rhodamine B via the Fenton reaction. Systematic experiments are performed to investigate the effects of pH, catalyst dosage, dye, and H2O2 concentrations and competitive anions on the rhodamine B degradation. Additionally, the Fenton photodegradation of RhB on CoFe2O4 is well-fitted to the first-order kinetic model. The redox pairs of Co(III)/Co(II) and Fe(III)/Fe(II) in the CoFe2O4 spinel structure might facilitate the formation of Fenton radicals, contributing to the decomposition of RhB through a proposed four-step mechanism. Notably, the material exhibits a strong magnetic response and maintains its excellent performance over five cycles, demonstrating the high potential for reusability as a photocatalyst.