Saldabilità di semilavorati Haynes® 282® riparati mediante saldatura con processo ad elettrodo infusibile

Fabian Hanning; Joel Håkan Andersson

Saldabilità di semilavorati Haynes® 282® riparati mediante saldatura con processo ad elettrodo infusibile
Journal article, 2019

This paper summarizes the results of test activities for the characterization of GTA welding pipes between low-alloy steel or alloy steel Gr. T22, T91 and T92 and 310HCbN stainless steel. In service condition, these dissimilar joints - for Ultra Super Critical (USC) power plant application - may be subjected to significant microstructure modifications which can affect their performance or even promote crack initiation and propagation. Through a relevant number of tests, the most significant combinations of base and filler materials were evaluated in comparative terms (using non-destructive and destructive testings) in order to evaluate - among other things - the influence of post weld heat treatment filler material and aging conditions of the welded joint.

cracking

multirun welding

post weld heat treatment

in service operations

Nickel alloys

heat resisting materials

GTA welding

strain ageing

Inconel

gas turbines

discs

repair

Author

Fabian Hanning

Chalmers, Industrial and Materials Science, Materials and manufacture

Other publications Research

Joel Håkan Andersson

University West

Other publications Research

Rivista Italiana della Saldatura

0035-6794 (ISSN)

1 27-37

Subject Categories (SSIF 2011)

Manufacturing, Surface and Joining Technology

More information

Latest update

1/10/2025

Saldabilità di semilavorati Haynes® 282® riparati mediante saldatura con processo ad elettrodo infusibile Journal article, 2019