Skador på skyddsmantlade plaströr vid grävningsfri förläggning
Report, 2005

This project aims at evaluating an external coating on plastics pipes, and its protective function against scratches and scoring damage from trenchless laying techniques. PE100 pressure pipes with four different coatings were tested in horizontal drilling and pipe bursting field-trials. During the tests, the lengthwise and cross-sectional deformations of the pipe were measured along with the traction force. The pipes’ surfaces were examined with respect to scratches, and the depth of the most prominent ones were determined. Of the two laying techniques, pipe bursting was the one causing the deepest scratches. Horizontal drilling was not significantly worse than ordinary handling during transport and preparation with respect to scratch depth. Dragging of the pipe above ground on asphalt surfaces caused severe damage to the pipe wall. The deepest scratches were seen on two pipe alternatives with soft coatings. Due to thic kness, however, these coatings were not penetrated and thus successfully protected the main pipe wall. The hardest coating tested, a polypropylene alternative, were also the thinnest one, and was penetrated at one location during the pipe bursting test. The traction force on the pipe was significantly higher during horizontal drilling than during pipe bursting. On the other hand, ovalisation of the pipe’s cross-section was greater during pipe bursting.

Horizontal drilling


pipe bursting


coated pipes


Stefan Forsaeus Nilsson

Kristian Thörnblom

Chalmers, Chemical and Biological Engineering, Polymer Technology

Areas of Advance

Building Futures (2010-2018)

Subject Categories

Infrastructure Engineering

More information