Development of nanocomposites based on organically modified montmorillonite and plasticized PVC with improved barrier properties

Journal article, 2015

Montmorillonite (MMT) was organically modified with tributyl citrate (TBC). Organoclays (OMMTs) were processed with diisononyl phthalate (DINP)-plasticized polyvinyl chloride (PVC) to form polymer nanocomposites. The produced composite materials showed a contradictory change in properties to that expected of a layered silicate nanocomposite, with a decreased E-modulus and increased gas permeability compared with a material without OMMT. It was experimentally shown that the TBC modifier was extracted from the OMMT and was dispersed in the PVC/DINP matrix, whereupon the OMMT collapsed and formed micrometer-sized agglomerates. Further investigation revealed that TBC has a significant effect on the gas permeability and the E-modulus, even at low additions to a DINP-plasticized PVC. A PVC nanocomposite with the TBC acting as both the OM for MMT and as the primary plasticizer was produced. This material showed a significantly increased E-modulus as well as a decrease in gas permeability, confirming that it is possible to develop a nanocomposite based on plasticized PVC, if both the organo-modification of the MMT and the formulation of the matrix are carefully selected