Effect of water-vapor-induced Cr vaporization on the oxidation of austenitic stainless steels at 700 and 900 degrees C - Influence of Cr/Fe ratio in alloy and Ce additions
Journal article, 2004

The oxidation of 153MA, 310 and 353MA austenitic stainless steels was investigated at 700°C and 310 and 353MA at 900°C in O 2 and in O 2 + 40% H 2 O. 153MA was not studied at 900°C because it suffered excessive corrosion. The influence of gas velocity was studied. The oxidized samples were investigated by grazing angle X-ray diffraction, scanning electron microscopy/energy dispersive analysis by X-rays Auger-electron spectroscopy, and glow discharge optical emission spectroscopy. In the presence of water vapor, gas velocity strongly influenced oxidation. This effect is attributed to chromium evaporation in the form of CrO 2 (OH) 2 . Exposure in O 2 + 40% H 2 O at 700°C using high flow rates caused breakaway corrosion on all alloys. At 900°C, only the 310 and 353MA alloys were investigated. In O 2 + H 2 O environment, both alloys showed a mass loss at low flow rates due to chromium evaporation. At high flow rates, alloy 310 suffered breakaway corrosion while 353MA did not. The corrosion products consisted of a relatively thin Cr-rich (Cr,Fe) 2 O 3 oxide plus thick, iron-rich oxide islands. The greater corrosion resistance of 310 and 353MA steels in environments where chromium evaporation is a factor is attributed to the high Cr/Fe ratio. In contrast, the presence of Ce and Si in the MA grade steels appears to have little beneficial effect on breakaway corrosion triggered by Cr evaporation. © 2004 The Electrochemical Society. All rights reserved.

flow-rate

high-temperature oxidation

oxide hydroxide evaporation

elements

corrosion

304l

scales

11-percent chromium steel

Author

Henrik Asteman

University of Gothenburg

Jan-Erik Svensson

Chalmers, Department of Environmental Inorganic Chemistry

Lars-Gunnar Johansson

University of Gothenburg

Journal of the Electrochemical Society

0013-4651 (ISSN) 1945-7111 (eISSN)

Vol. 151 3 B141-B150

Subject Categories

Manufacturing, Surface and Joining Technology

DOI

10.1149/1.1644138

More information

Created

10/8/2017