Influence of the platinum-support interaction on the direct reduction of NOx under lean conditions

Journal article, 1998

Catalysts containing Pt supported on SiC, Al2O3 and ZSM-5 were prepared and studied for NOx reduction by C3H6 in Oz excess under transient (temperature ramps) and steady-state conditions. The maximum NOx reduction activity in the heating ramp experiments was similar for Pt/SiC and Pt/ZSM-5, while Pt/Al2O3 showed higher maximum activity. Both N-2 and N2O formation was observed for all catalysts, although the respective amounts varied with the investigated system. Highest Nz selectivity was observed for Pt/Al2O3. When the NOx reduction activity was studied under steady-state conditions the activity of Pt/Al2O3 decreased substantially (mainly due to a loss in N-2 production). Pt/ZSM-5 became somewhat more selective towards Na production whereas the activity and selectivity of Pt/SiC remained at about the same values as far the heating ramp experiments. Adsorbed species on the surface of the different catalysts were investigated using in-situ FTIR in order to obtain information about the reaction mechanisms. The adsorption of species on Pt/SiC was negligible, while a number of absorption bands were observed for Pt/Al2O3 (N and C containing species, and -NCO) and Pt/ZSM-5 (HC).