This work reports the polymerization of 1-octene to yield semicrystalline, branched poly(ethylene) like materials with high molecular weight and narrow molecular weight distribution. The polymerization of 1-octene was catalyzed by an alpha-diimine Ni(II) complex [(ArN)C(CH3)-(CH3) C(NAr)]NiBr2 [Ar = 2,6-(iPr)(2)C6H3], in combination with different aluminum alkyls, i.e., Et2AlCl, MAO and MMAO. The effect of the aluminum alkyl, monomer concentration, polymerization temperature and Al/Ni ratio on the activity, selectivity of monomer insertion, polymers microstructure, and structure/properties is investigated. The results indicate the possibility to tune the polymer microstructure, which in turn strongly affects the structure, thermal and mechanical polymer properties. Mechanical testing carried out by uniaxial stretching until failure and step-cycle tensile experiments served to establish these materials as a new class of polyolefin thermoplastic elastomers with different performances depending on the microstructure and crystallinity.

Thermoplastic elastomers

Mechanical properties

Nickel

1-Octene polymerization

Polyolefins

Author

G. Leone

Consiglo Nazionale Delle Richerche

Massimiliano Mauri

Chalmers, Chemistry and Chemical Engineering, Applied Chemistry

I. Pierro

Consiglo Nazionale Delle Richerche

University of Naples Federico II

G. Ricci

Consiglo Nazionale Delle Richerche

M. Canetti

Consiglo Nazionale Delle Richerche

F. Bertini

Consiglo Nazionale Delle Richerche

Polymer

0032-3861 (ISSN)

Vol. 100 37-44

Subject Categories

Polymer Chemistry

DOI

10.1016/j.polymer.2016.08.009

More information

Latest update

9/6/2018 1