Superconductivity in Sr2RuO4-Sr3Ru2O7 eutectic crystals
Artikel i vetenskaplig tidskrift, 2008
Superconducting behavior has been observed in the Sr2RuO4-Sr3Ru2O7 eutectic system as grown by the flux-feeding floating-zone technique. A supercurrent flows across a single interface between Sr2RuO4 and Sr3Ru2O7 areas at distances that are far beyond those expected in a conventional proximity effect. The current-voltage characteristics within the Sr3Ru2O7 macrodomain, as extracted from the eutectic, exhibit signatures of superconductivity in the bilayered Sr3Ru2O7 region. Detailed microstructural, morphological and compositional analyses address issues on the concentration and the size of Sr2RuO4 inclusions within the Sr3Ru2O7 matrix. We speculate on the possibility of inhomogeneous superconductivity in the eutectic Sr3Ru2O7 and exotic pairing induced by the Sr2RuO4 inclusions. Copyright (C) EPLA, 2008.
SR2RUO4
SR3RU2O7
Författare
R. Fittipaldi
Istituto Nazionale per la Fisica della Materia
Universita degli Studi di Salerno
A. Vecchione
Universita degli Studi di Salerno
Istituto Nazionale per la Fisica della Materia
Regina Ciancio
Istituto Nazionale per la Fisica della Materia
Universita degli Studi di Salerno
Chalmers
S. Pace
Universita degli Studi di Salerno
Istituto Nazionale per la Fisica della Materia
M. Cuoco
Universita degli Studi di Salerno
Istituto Nazionale per la Fisica della Materia
D. Stornaiuolo
Universita degli Studi di Napoli Federico II
D. Born
Universita degli Studi di Napoli Federico II
F. Tafuri
Universita degli Studi di Napoli Federico II
Università degli Studi della Campania Luigi Vanvitelli
Eva Olsson
Chalmers, Teknisk fysik, Mikroskopi och mikroanalys
S. Kittaka
Kyoto University
H. Yaguchi
Kyoto University
Y. Maeno
Kyoto University
Europhysics Letters
0295-5075 (ISSN) 1286-4854 (eISSN)
Vol. 83 2 Art. no. 27007- 27007Ämneskategorier
Annan teknik
DOI
10.1209/0295-5075/83/27007