Low temperature CO oxidation over supported ultrathin MgO films
Artikel i vetenskaplig tidskrift, 2009

Density functional theory is used to investigate CO oxidation over an ultrathin MgO film supported on Ag(100). O-2 is found to be activated on MgO/Ag(100) whereas CO is only weakly bonded to the surface. These adsorption properties together with a low activation barrier render the MgO/Ag system an efficient catalyst for CO oxidation at low temperatures. As the predicted mechanism is general in nature, the result is suggested to have implications for a wide range of oxidation reactions.

Catalysis

CO oxidation

Nano

Materials

Författare

Anders Hellman

Chalmers, Teknisk fysik, Kemisk fysik

Kompetenscentrum katalys

Simon Klacar

Chalmers, Teknisk fysik, Kemisk fysik

Kompetenscentrum katalys

Henrik Grönbeck

Kompetenscentrum katalys

Chalmers, Teknisk fysik, Kemisk fysik

Journal of the American Chemical Society

0002-7863 (ISSN) 1520-5126 (eISSN)

Vol. 131 46 16636-16637

Drivkrafter

Hållbar utveckling

Styrkeområden

Nanovetenskap och nanoteknik

Transport

Energi

Materialvetenskap

Fundament

Grundläggande vetenskaper

Ämneskategorier

Atom- och molekylfysik och optik

DOI

10.1021/ja906865f

Mer information

Skapat

2017-10-08