Synthesis, structure and magnetic properties of Sr2Fe1-xGaxMoO6 (0 <= x <= 0.6) double perovskites
Artikel i vetenskaplig tidskrift, 2009
Polycrystalline Sr2Fe1-xGaxMoO6 (0 <= x <= 0.6) materials have been synthesized by solid state reaction method and studied by neutron powder diffraction (NPD) and magnetization measurements. Rietveld analysis of the temperature dependent NPD data shows that the compounds crystallize in the tetragonal symmetry in the space group 14/m. The anti-site (AS) defects concentration increases with Ga doping, giving rise to highly B-site disordered materials. Ga doping at the Fe-site decreases the cell volume. The evolution of bond lengths and the cation oxidation states was determined from the Rietveld refinement data. The saturation magnetization and Curie temperature decreased with the increasing Ga content in the samples. Low temperature neutron diffraction data analysis and magnetization measurements confirm the magnetic interaction as ferrimagnetic in the sample. (C) 2009 Elsevier Ltd. All rights reserved.
room-temperature
Chemical synthesis
Neutron diffraction
Magnetic properties
Oxides
Crystal structure
magnetoresistance
sr2femoo6
ba
curie-temperature