Neutron powder diffraction study of Pb(HfxTi1-x)O-3 ceramics (0.10 <= x <= 0.50)
Artikel i vetenskaplig tidskrift, 2005

The crystal symmetries of lead hafnate titanate (Pb(HfxTi1-x)O-3, PHT) powders with 0.10 <= x <= 0.50 were investigated by high-resolution neutron powder diffraction. Samples with x <= 0.40 were tetragonal (space group P4mm), while the sample with x = 0.50 contained both monoclinic Cm and rhombohedral (modeled using the R3c space group) phases. The role of the B cations (Hf and Ti) and the oxygen octahedra network, in addition to the displacement of Pb ions from their ideal sites, in promoting the phase transformation between the P4mm and Cm phases was considered. Two types of structural disorder were identified. Diffuse scattering between Bragg reflection peaks was assigned to Pb ion displacement. A second type of structural disorder, revealed by the weak intensities of observed pseudo-cubic 00/ reflections with / even and as 001 reflection peak widths significantly broader than the 100 reflection peaks, was observed. This behavior was attributed to disorder in the arrangement of the O-B-O rows parallel to the c axis. For small values of x, this shift was predominantly along the c axis, whereas shifts perpendicular to the c axis increased with increasing x. These features were modeled using an hkl-dependent line-broadening model. The origin of the W-dependent line broadening was assigned to the microstrain accompanying a spatial-composition variation. Structural models were tested by computing valence sums and spontaneous polarization values.

PEROVSKITE

MODEL

SOLID-SOLUTION

KeyWords Plus: MONOCLINIC PHASE

PBZR0.52TI0.48O3

FERROELECTRIC PROPERTIES

LEAD TITANATE

Författare

J Frantti

Y Fujioka

Sten Eriksson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

S Hull

M Kakihana

Inorganic Chemistry

0020-1669 (ISSN) 1520-510X (eISSN)

Vol. 44(25) 9267-9278

Ämneskategorier

Miljövetenskap

Mer information

Skapat

2017-10-06