Catalytic behavior and characterization of (CuO)1-z(La2O3)z/2 based catalysts deposited on γ-Al2O3 and prepared in situ with 0.0≤z≤1.00 with and without addition of Pd
Artikel i vetenskaplig tidskrift, 1996

(CuO)(1-z)(La2O3)(z/2) based catalysts with 0.0 less than or equal to z less than or equal to 1.0 supported on gamma-Al2O3 have been prepared in situ and the phases formed have been identified by XRD, SEM and TEM/EDS studies. The catalyst with z = 0.5 exhibited the best catalytic activity for oxidation of CO (T-50 = 295 and 390 degrees C with degrees of conversions of 93 and 92% at 450 degrees C under rich and lean conditions, respectively) and C3H6 (291 and 414 degrees C; 93 and 83%) and reduction of NO (405 degrees C; 60 and 0%). This catalyst contained appreciable amounts of the perovskite phase LaAl1-xCuxO3 and the enhanced catalytic properties are ascribed to the presence of this phase. Addition of Pd to this catalyst implied that the degree of conversion of NO increased and that the light-off temperatures for all involved gas species decreased. Ageing experiments revealed that LaAl1-xCuxO3 decomposed and that Cu containing Pd particles were formed during this procedure which in turn deteriorated the catalytic properties of the catalyst.

CuO-La2O3-Al2O3

Pd

Oxide based catalysts

SEM-TEM/EDS

XRD

Författare

Leif Dahl

Kjell Jansson

Mats Nygren

Magnus Skoglundh

Kompetenscentrum katalys

Institutionen för teknisk kemi

Catalysis Letters

1011-372X (ISSN) 1572-879X (eISSN)

Vol. 37 1-2 69-77

Drivkrafter

Hållbar utveckling

Styrkeområden

Nanovetenskap och nanoteknik

Transport

Energi

Materialvetenskap

Ämneskategorier

Kemiteknik

DOI

10.1007/BF00813522

Mer information

Skapat

2017-10-07