Polymethylmethacrylate (PMMA) based quasi-solid electrolyte with binary iodide salt for efficiency enhancement in TiO2 based dye sensitized solar cells
Artikel i vetenskaplig tidskrift, 2014
Enhancement of efficiency by using iodide mixture (Pr4NI and I(1), instead of a single iodide salt, in N719 dye-sensitized solar cells with a polymethylmethacrylate (PMMA) based gel electrolyte is investigated. The salt ratio is varied to optimize efficiency. With 100 wt.% KI and 100 wt.% (Pr4NI) efficiencies under AM 1.5 illumination are 3.39% and 3.21%, while 22.2:77.8 wt.% ratio KI:Pr4NI shows the highest efficiency of 3.99%. This is an efficiency enhancement of 18%. Variation of efficiency with salt composition appears to correspond to the change in short circuit photocurrent density (J(sc)) and the iodide ion conductivity.
gel polymer electrolyte
lithium
transport
charge-injection
conversion
batteries
nanocrystalline tio2
plasticized electrolyte
photovoltaic performance
conductivity
Författare
M.A.K.L. Dissanayake
Chalmers, Teknisk fysik, Fasta tillståndets fysik
R. Jayathissa
University of Peradeniya
VA Seneviratne
University of Peradeniya
C. A. Thotawatthage
National Institute of Fundamental Studies
G. K. R. Senadeera
Open University of Sri Lanka
National Institute of Fundamental Studies
Bengt-Erik Mellander
Chalmers, Teknisk fysik, Nukleär teknik
Solid State Ionics
0167-2738 (ISSN)
Vol. 265 85-91Drivkrafter
Hållbar utveckling
Styrkeområden
Nanovetenskap och nanoteknik
Energi
Materialvetenskap
Ämneskategorier
Fysik
DOI
10.1016/j.ssi.2014.07.019