Triplet superconductivity in oxide ferromagnetic interlayer of mesa-structure

Paper i proceeding, 2014

We present experimental data on Nb-Au/La0.7Sr0.3MnO3/SrRuO3/YBa2Cu3O7-δ mesa- structure with in plane linear size 10÷50 μm. The mesa-structures were patterned from the epitaxial heterostructures fabricated by pulsed laser ablation and magnetron sputtering. Superconducting critical current was observed for mesa-structures with the interlayer thicknesses up to 50 nm. In the mesa-structures with just one, either La0.7Sr0.3MnO3 or SrRuO3 interlayer with a thickness larger than 10 nm no superconducting current was observed. The registered superconducting current for the mesa-structures with a thinner interlayer is attributed to pinholes. Obtained results are discussed in terms of superconducting long-range triplet generation at interfaces of superconductor and a composite ferromagnet consisting of ferromagnetic materials with non-collinear magnetization.