Electrical, mechanical, and thermal properties of LDPE graphene nanoplatelets composites produced by means of melt extrusion process
Artikel i vetenskaplig tidskrift, 2017

Composites of LDPE filled with different amounts of graphene nanoplatelets (GnP) were prepared in form of films by means of precoating technique and single screw melt- extrusion using two types of screws, compression and mixing. This manufacturing process imposes strong anisotropy on the sample's morphology, in which the nanoplatelets become oriented along the extrusion direction. Such orientation of GnP in LDPE matrix is confirmed by scanning electron microscopy observations and it yields unique electrical properties. As compared to pure LDPE, significant reductions of the through- plane conductivity are found for the composites at relatively low electric fields (< 20 kV/mm) at low filler concentrations. Above the field level of 20 kV/mm, a crossover effect is observed that results in a strong field dependency of the conductivity where the non- linear behavior starts to dominate. Moreover, differential scanning calorimetry (DSC) results indicate a decrease in polymer crystallinity of the composite matrix with increasing filler content, whereas thermogravimetric (TG) analysis shows a slight increase in the material's thermal stability. Application of GnP also leads to improvement of mechanical properties, manifested by the increase of Young's modulus and tensile strength in both types of samples.

graphene nanocomposites

thermal properties

dielectric response

field grading materials

mechanical properties

low density polyethylene

electrical conductivity

Författare

Karolina Gaska

Chalmers, Material- och tillverkningsteknik, Högspänningsteknik

Xiangdong Xu

Chalmers, Material- och tillverkningsteknik, Högspänningsteknik

Stanislaw Gubanski

Chalmers, Material- och tillverkningsteknik, Högspänningsteknik

Roland Kádár

Chalmers, Material- och tillverkningsteknik, Polymera material och kompositer

Polymers

2073-4360 (eISSN)

Vol. 9 1 11- 11

Drivkrafter

Hållbar utveckling

Styrkeområden

Nanovetenskap och nanoteknik

Energi

Materialvetenskap

Ämneskategorier

Kompositmaterial och -teknik

DOI

10.3390/polym9010011