Varestraint Weldability Testing of ATI 718Plus (R)-Influence of Eta Phase
Paper i proceeding, 2018

This study investigates the effect of eta phase on hot cracking susceptibility of ATI 718Plus (R). Two heat treatment conditions of 950 degrees C/1 h and 950 degrees C/15 h having different amounts of eta phase were tested by longitudinal Varestraint testing method. The heat treatment at 950 degrees C/15 h exhibited the highest amount of cracking. This was related to the higher amount of eta phase precipitation during the long dwell heat treatment which aided to extensive liquation during welding.

ATI 718plus (R)

Hot cracking

Varestraint testing

Eta phase

Författare

Sukhdeep Singh

Chalmers, Industri- och materialvetenskap, Material och tillverkning

William Fransson

Högskolan Väst

Joel Andersson

Högskolan Väst

Anssi Brederholm

Aalto-Yliopisto

Hannu Hanninen

Aalto-Yliopisto

Minerals, Metals and Materials Series

23671181 (ISSN) 23671696 (eISSN)

929-937
978-3-319-89480-5 (ISBN)

9th International Symposium on Superalloy 718 and Derivatives - Energy, Aerospace, and Industrial Applications
Champion, PA, USA,

Ämneskategorier

Bearbetnings-, yt- och fogningsteknik

Annan materialteknik

Metallurgi och metalliska material

DOI

10.1007/978-3-319-89480-5_62

Mer information

Senast uppdaterat

2024-01-03