Biaxial transverse compression testing for a fibre reinforced polymer material
Paper i proceeding, 2020

Unidirectional laminates have been tested under uniaxial transverse compression and under biaxial transverse compression. Failure occurred by shear in an inclined failure plane parallel to the fibres. The transverse shear response of the material on the failure plane was evaluated from the tests. In the biaxial tests, the failure load was considerably higher than in the uniaxial tests. For a given transverse shear strain the transverse shear stress was also higher in the case of biaxial compression. It is also shown that using waisted specimens instead of prismatic specimens does not seem to bring noticeable benefits for through-thickness uniaxial compression tests. The experimental results presented here are important input to the development and the validation of damage models of fibre reinforced polymer materials accounting for the matrix nonlinear response in shear and compression.

Polymer matrix composites

Biaxial testing

Författare

Thomas Bru

Chalmers, Industri- och materialvetenskap, Material- och beräkningsmekanik

Swerea

Leif Asp

Chalmers, Industri- och materialvetenskap, Material- och beräkningsmekanik

R. Olsson

Swerea

Gaurav Vyas

Swerea

ECCM 2018 - 18th European Conference on Composite Materials

18th European Conference on Composite Materials, ECCM 2018
Athens, Greece,

Styrkeområden

Transport

Energi

Materialvetenskap

Ämneskategorier

Teknisk mekanik

Annan materialteknik

Kompositmaterial och -teknik

Mer information

Senast uppdaterat

2024-01-03