Effect of alloying elements in Ni-base substrate material on interdiffusion processes in MCrAlY-coated systems
Artikel i vetenskaplig tidskrift, 2018

he effect of alloying elements in the substrate on the interdiffusion processes between a NiCoCrAlY-coating and model Ni-base superalloys was studied. Four single-crystal substrates Ni-10Cr-8Al-X (wt%, X = 10Co, 9Ta, 6 W) were coated with a conventional NiCoCrAlY-coating and exposed to air for up to 1000 h at 1050 °C. The microstructural analyses (LOM/SEM/EDX) revealed a strong dependence of the coating degradation rate on the substrate composition. The coating applied to the ternary base Ni-10Cr-8Al alloy and to the quaternary Co-containing substrate degraded most rapidly while the Ta addition to the substrate effectively suppressed interdiffusion. The degradation phenomena such as β-NiAl depletion and propagation of the secondary reaction zone (SRZ) were interpreted in terms of a thermodynamical analysis in Thermo-Calc and by using a CALPHAD-based thermodynamic-kinetic diffusion model.

Diffusion modelling

Författare

T. Galiullin

Forschungszentrum Jülich

Anton Chyrkin

Chalmers, Fysik, Materialens mikrostruktur

Forschungszentrum Jülich

R. Pillai

Forschungszentrum Jülich

R. Vassen

Forschungszentrum Jülich

W. J. Quadakkers

Forschungszentrum Jülich

Surface and Coatings Technology

0257-8972 (ISSN)

Vol. 350 359-368

Ämneskategorier

Bearbetnings-, yt- och fogningsteknik

Metallurgi och metalliska material

Korrosionsteknik

DOI

10.1016/j.surfcoat.2018.07.020

Mer information

Senast uppdaterat

2018-10-18