Impact of tetrabutylammonium, iodide and triiodide ions conductivity in polyacrylonitrile based electrolyte on DSSC performance
Artikel i vetenskaplig tidskrift, 2020

Gel polymer electrolytes (GPEs) with polyacrylonitrile (PAN)-based polymer, ethylene carbonate (EC) and propylene carbonate (PC) plasticizers, and different amounts of tetrabutylammonium iodide (TBAI) salt and iodine (I-2) have been prepared and used in dye-sensitized solar cells (DSSCs). The maximum room temperature conductivity of 5.14 mS cm(-1) is obtained for electrolyte with a composition of 8 wt% PAN-30 wt% EC-30 wt% PC-30 wt% TBAI-2 wt% I-2 (S3 electrolyte) which influenced by the highest charge carrier density of 7.93 x 10(20) cm(-3) estimated from fitting the impedance Nyquist plot. The DSSC fabricated with S3 electrolyte revealed the highest power conversion efficiency of 3.45% with open-circuit voltage (V-oc) of 582 mV and short-circuit current density (J(sc)) of 12.9 mA cm(-2) . The incident photon-to-current conversion efficiency of the DSSC with highest efficiency is 54.01%. The electrical impedance spectroscopy of the same cell shows the lowest series resistance indicating the superiority of electrolyte charge transport characteristics in DSSC. In addition, electron transfer time constant (tau(t)(r)) and electron recombination time (tau(rec)), charge collection efficiency (eta(cc)), electron diffusion coefficient (D) and diffusion length (L-D) of DSSC fabricated with GPEs prepared have been estimated by intensity-modulated photocurrent spectroscopy and intensity-modulated photovoltage spectroscopy techniques. The DSSC with highest efficiency shows lowest tau(t)(r), of 34.46 ms and highest tau(rec), of 90.41 ms due to the huge amount of TBA(+) ions that covered the surface area of mesoporous TiO2. The eta(cc )of 0.62, D of 4.00 x 10(-5) cm(2) s(-1) and L-D of 19.02 mu m further support the photovoltaic efficiency of DSSC.

Electron transfer time constant

Dye-sensitized solar cells

Electrical transport properties

Electron recombination time

Diffusion length

Författare

Faisal I. Chowdhury

University of Chittagong

M. H. Buraidah

University of Malaya

A. K. Arof

University of Malaya

Bengt-Erik Mellander

Subatomär, högenergi- och plasmafysik

I. M. Noor

Universiti Putra Malaysia

Solar Energy

0038-092X (ISSN)

Vol. 196 379-388

Ämneskategorier

Energiteknik

Materialkemi

DOI

10.1016/j.solener.2019.12.033

Mer information

Senast uppdaterat

2020-03-06