Corrosion Behavior of WC-Co-(Ni)-(Cr) Cemented Carbide in Neutral Solution
Artikel i vetenskaplig tidskrift, 2020

Three groups of WC-Co-(Ni)-(Cr) cemented carbides with different binder phase compositions were prepared by powder metallurgy using WC, Co, Ni and Cr3C2 powders as raw materials. The corrosion behavior of the three alloys in neutral solution was studied by polarization curve test and immersion experiment. The corrosion mechanism was discussed by means of scanning electron microscopy, energy spectrum analysis, X-ray photoelectron spectroscopy (XPS) and EBSD. The results show that in neutral solution the corrosion of WC-Co and WC-Co-Cr cemented carbides is mainly caused by the selective dissolution of Co and the corrosion products after immersion are mainly composed of Co(OH)2. The corrosion resistance of WC-Co cemented carbide in neutral solution can be improved by the addition of Cr, which may be related to the decrease in the content of hcp-Co in the binder phase by adding Cr. Adding Ni and Cr together can further improve the corrosion resistance of WC-Co cemented carbide in neutral solution. After immersion for 480 h in Na2SO4 solution, the WC-Co-Ni-Cr alloy sample is just corroded slightly.

Ni

Corrosion

XPS

Cr C 3 2

Cemented carbide

Författare

Xiuyu Wei

State Key Laboratory of Cemented Carbide

Zhuzhou Cemented Carbide Group Corp. Ltd.

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Peng Jin

Zhuzhou Cemented Carbide Group Corp. Ltd.

State Key Laboratory of Cemented Carbide

Yanping Xia

State Key Laboratory of Cemented Carbide

Zhuzhou Cemented Carbide Group Corp. Ltd.

Huaimin Yu

State Key Laboratory of Cemented Carbide

Zhuzhou Cemented Carbide Group Corp. Ltd.

Weibing Zhang

State Key Laboratory of Cemented Carbide

Zhuzhou Cemented Carbide Group Corp. Ltd.

Yu Cao

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

1002-185X (ISSN)

Vol. 49 1 313-319

Ämneskategorier

Annan kemi

Metallurgi och metalliska material

Korrosionsteknik

Mer information

Senast uppdaterat

2020-05-19