[Person e6de5c41-75a8-4100-a31e-94d13d4890b2 not found]; [Person 57b4e3d2-7939-4a1a-9a45-ce1a65a24e43 not found]; [Person 31d4cf1e-24b6-406d-a4c1-76ccab5127c5 not found]; [Person 86118ef8-7b72-46ac-96da-85657eb32244 not found]; [Person 666702c4-23f3-4d0c-b3d8-fd1011179439 not found]; [Person b225edd1-008a-48de-bd6e-169a64068f25 not found]; [Person 72cd8b10-b842-435d-9aee-dc8bc3b7c161 not found]; [Person 98c44713-9148-47a1-aeee-c92ae678a33e not found]; [Person edb6b496-b57b-43b2-b71b-f89b6068e23a not found]

doi:10.1007/s10854-024-13837-1

Dye-sensitized solar cells achieved with multi-layered SnO₂/ZnO composite photoanodes through precise control of thickness and composition
Artikel i vetenskaplig tidskrift, 2024

The spin coating is cost-effective, straightforward, and highly suitable for the large-scale production of solar cells. In this study, we report the fabrication of SnO2/ZnO composite films for dye-sensitized solar cells (DSCs) using a simplified and cost-effective spin-coating technique on fluorine-doped tin oxide glass substrates. This study introduces a new way of preparing a multi-layered composite thin film using a suspension containing colloidal SnO2 nanoparticles and ZnO nanoparticles followed by sonication and aging of TiO2-free high-efficiency DSCs. Our approach provides a facile way of obtaining a uniform film of tunable thickness with high reproducibility by adjusting the total number of coating cycles. The spin-coating process achieved a nano-sized SnO2-covered ZnO layer, contributing to enhanced conversion efficiency in DSCs. A specific number of seven coating cycles was identified as optimal for achieving the aspirational performance. Under standard AM 1.5 irradiation with an intensity of 100 mW/ cm2, the fabricated SnO2/ZnO composite films revealed an overall energy conversion efficiency of 6.5% with a thickness of 2.06 mu m which is impressive for a TiO2-free DSC. This achievement indicates the potential of the developed fabrication process for cost-effective and scalable production of efficient DSCs with SnO2/ZnO composite.