Superconducting weak bonds at grain boundaries in MgB2
Artikel i vetenskaplig tidskrift, 2007

The possibility of preparing bicrystalline Josephson junctions and bolometers based on superconducting MgB2 on specially prepared bicrystalline MgO substrates is investigated. Microbridges 0.85–6.00 μm in width, intersecting the bicrystalline interface, are formed in epitaxial bicrystalline MgB2 films grown on these substrates. It is found that annealing of bicrystalline samples in oxygen leads to a systematic decrease in the critical current, an increase in the temperature width of the superconducting transition region, and to an improvement of the current-voltage (IV) characteristic, which becomes close in shape to the IV characteristic of a Josephson junction. The response of such a junction to radiation at a frequency of 110 GHz with an amplitude attaining 0.5 mV is measured.



weak links


Mikhail Tarasov

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Evgeni Stepantsov

Michio Naito

A. Tsukada

Dag Winkler

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Alexei Kalaboukhov

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

M.Yu. Kupriyanov

JETP Letters

0021-3640 (ISSN) 1090-6487 (eISSN)

Vol. 105 3 636-641


Den kondenserade materiens fysik

Mer information