Sol-gel-derived potassium-based di-ureasils for "smart windows''
Artikel i vetenskaplig tidskrift, 2007

Sol-gel-derived KCF3SO3-doped di-urea cross-linked poly(oxyethylene) (POE)/siloxane (di-ureasil) ormolytes with infinity > n >= 1 (n is the number of oxyethylene units per K+ ion) have been analysed. Samples with n. 40 are thermally stable up to 310 degrees C. At n >= 100, POE crystallites are present. At n = 5, a crystalline POE-KCF3SO3 complex with stoichiometry 1 : 1 is formed. In the xerogel with n = 1 this complex coexists with free salt. The highest ionic conductivity is reached at n = 20. The redox stability domain of this material spans 5.0 V. "Free'' anions and weakly coordinated CF3SO3- ions appear to be the main charge carriers at n = 20. The K+ ions interact with the urea carbonyl oxygen atoms at all salt concentrations. Complexation of the cations by POE occurs at n <= 20. In the latter composition range, contact ion pairs and higher ionic aggregates develop. The ormolytes were successfully used in the assembly of prototype electrochromic devices (ECDs) that exhibit good electrochemical stability and demonstrate a memory effect. The ECD incorporating the ormolyte with n = 20 displays an average transmittance in the visible region of ca. 90% in the coloured state and of 85-95 % in the bleached state. The corresponding change in colour, evaluated on the basis of the Commission Internationale d'Eclairage (CIE) colour-coordinates system, is reversible: from yellow (0.38, 0.37) for the bleached state to blue (0.29, 0.29) for the coloured state.

IONIC-CONDUCTIVITY

SPECTRA

ORMOLYTES

SALTS

TEMPERATURE

POLYMER ELECTROLYTES

FILMS

STATE

TRIFLATE

ENVIRONMENT

Författare

S. C. Nunes

Universidade de Tras-os-Montes e Alto Douro

V. D. Bermudez

Universidade de Tras-os-Montes e Alto Douro

M. M. Silva

Universidade do Minho

M. J. Smith

Universidade do Minho

Denis Ostrovskii

Chalmers, Teknisk fysik, Kondenserade materiens fysik

R. A. S. Ferreira

Centro de Investigacao em Materiais Ceramicos e Compositos

L. D. Carlos

Centro de Investigacao em Materiais Ceramicos e Compositos

J. Rocha

Centro de Investigacao em Materiais Ceramicos e Compositos

A. Goncalves

Universidade do Porto

E. Fortunato

Universidade do Porto

Journal of Materials Chemistry

0959-9428 (ISSN) 1364-5501 (eISSN)

Vol. 17 4239-4248

Ämneskategorier

Annan teknik

DOI

10.1039/b708905h