Role of Pt-precursor on the performance of Pt/BaCO3/Al2O3 NOx storage catalysts
Artikel i vetenskaplig tidskrift, 2005

The influence of the choice of platinum precursor on the catalytic performance of Pt/BaCO3/Al2O3 NO, storage catalysts was studied. The precursors used in the preparation of the catalysts were: (i) hexachloroplatinic acid [H2Pt(Cl)(6)], (ii) tetraammineplatinum hydroxide [Pt(NH3)(4)(OH)(2)], (iii) diammineplatinum nitrite [Pt(NH3)(2)(NO2)(2)] and (iv) platinum nitrate [Pt(NO3)(2)]. The catalytic activity of the prepared catalysts was tested for continuous lean NOx reduction with C3H6, NOx storage and reduction, and NO2 dissociation in a flow reactor. The reactor experiments show that the sample prepared using platinum nitrate is the most active catalyst followed by the catalyst prepared from tetraammineplatinum hydroxide. The catalyst prepared from hexachloroplatinic acid is more active for continuous NOx reduction, and NO2 storage and reduction than the catalyst prepared from diammineplatinum nitrite, but deactivates faster during NO2 dissociation than the catalyst prepared using diammineplatinum nitrite.

NOX STORAGE

ADSORPTION

NOBLE-METAL

DISTRIBUTIONS

DECOMPOSITION

SULFUR DEACTIVATION

GAMMA-ALUMINA

EXPOSURE CONDITIONS

PT/BAO/AL2O3

NO(X) STORAGE

Författare

JAZAER DAWODY

Chalmers, Teknisk fysik, Kemisk fysik

Kompetenscentrum katalys (KCK)

Magnus Skoglundh

Kompetenscentrum katalys (KCK)

Chalmers, Kemi- och bioteknik

S. Wall

Göteborgs universitet

Erik Fridell

Chalmers, Teknisk fysik, Kemisk fysik

Kompetenscentrum katalys (KCK)

Journal of Molecular Catalysis A: Chemical

1381-1169 (ISSN)

Vol. 225 2 259-269

Drivkrafter

Hållbar utveckling

Styrkeområden

Nanovetenskap och nanoteknik

Transport

Energi

Materialvetenskap

Ämneskategorier

Fysik

Kemiteknik

DOI

10.1016/j.molcata.2004.09.011