Morphological and chemical characterization of tooth enamel exposed to alkaline agents
Artikel i vetenskaplig tidskrift, 2010

Objectives: In this study, morphological and chemical changes in teeth enamel exposed to alkaline agents, with or without surfactants, have been investigated. In addition, chemical effects of the organic surface layer, i.e. plaque and pellicle, were also investigated. Methods: The present study was conducted using several techniques: Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Results: From XPS-measurements, it was found that exposure to alkaline solutions resulted in a massive removal of carbon from the tooth surface, and that the addition of surfactants increased the rate under present conditions. Based on the results from the FTIR-analysis, no substitution reactions between phosphate, carbonate and hydroxide ions in the enamel apatite could be detected. From a minor SEM-analysis, degradation and loss of substance of the enamel surface was found for the exposed samples. From XRD-analysis, no changes in crystallinity of the enamel apatite could be found between the samples. Conclusions: The findings in this study show that exposure to alkaline solutions results in a degradation of enamel surfaces very dissimilar from acidic erosion. No significant erosion or chemical substitution of the apatite crystals themselves could be discerned. However, significant loss of organic carbon at the enamel surface was found in all exposed samples. The degradation of the protective organic layer at the enamel surface may profoundly increase the risk for caries and dental erosion from acidic foods and beverages.

Enamel

Odontology

SEM

XRD

Biofilm

FTIR

Alkaline

Erosion

XPS

Dental

Författare

Fabian Taube

Göteborgs universitet

Rikard Ylmén

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

A. Shchukarev

S. Nietzsche

Jörgen G Norén

Göteborgs universitet

Journal of Dentistry

0300-5712 (ISSN) 1879-176X (eISSN)

Vol. 38 1 72-81

Ämneskategorier

Odontologi

DOI

10.1016/j.jdent.2009.09.006

Mer information

Skapat

2017-10-06