Fabrication of arrays of nanometer size test structures for scanning probe microscope tips characterization
Paper i proceeding, 1994

A problem in scanning probe microscopy (SPM) is the unknown shape of the probing tip. Generally, the image is a convolution between the shape of the tip and the surface. Information of the shape of the probe may be gained by imaging very sharp tips. Here we present a method for making two-dimensional arrays of very sharp tips. The tip arrays were made of silicon using electron beam lithography with subsequent ion-beam etching. To achieve the best possible resolution, ultrasonic excitation was used during development of the bilayered PMMA resist. Thus, openings in the resist with size nearly equal to the spot size of the writing e-beam have been obtained. A further decrease of the radius of the tips was obtained by the choice of appropriate thickness for the masking NiCr layer. The tips were conical with a height up to 100 nm with a radius of the tip down to 10 nm. The tips were suitable for study of the shape of AFM probe tips, under condition that the tip array samples were rinsed in water prior to the measurement. Without the rinsing procedure, strong sticking forces between the probe and the sample would have eroded both of them. The regularity of the array provided an easy way to calibrate the lateral motion of the scanner

electron beam lithography

scanning probe microscopy

atomic force microscopy


sputter etching


A. L. Bogdanov

Institutionen för fysik

D. Erts

Institutionen för fysik

Bengt Nilsson

Institutionen för fysik

Håkan Olin

Institutionen för fysik

Journal of Vacuum Science & Technology B: Microelectronics Processing and Phenomena

0734-211X (ISSN)

Vol. 12 6 3681-3684


Nanovetenskap och nanoteknik (SO 2010-2017, EI 2018-)



Övrig annan teknik



Mer information