Investigation into the growth and structure of thin-film solid solutions of iron-based superconductors in the FeSe0.92-FeSe0.5Te0.5 system
Artikel i vetenskaplig tidskrift, 2013

Thin films of FeSe0.92 and FeSe0.5Te0.5 iron chalcogenide superconductors and solid solutions containing these components in different ratios have been grown on the surface of LaAlO3 (102) crystals by pulsed laser deposition. Films of solid solutions have been deposited by simultaneous laser ablation from two targets of the FeSe0.92 and FeSe0.5Te0.5 stoichiometric compositions onto one substrate. An X-ray diffraction study of the film structure shows that the films grown are epitaxial and their lattice parameters regularly vary with the ratio of the deposited components, which was controllably varied by changing the ablation intensities from the targets.

Författare

Evgeni Stepantsov

Russian Academy of Sciences

S. M. Kazakov

Moscow State University

V. V. Belikov

Moscow State University

I. P. Makarova

Russian Academy of Sciences

Riccardo Arpaia

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Robert Gunnarsson

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Floriana Lombardi

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Crystallography Reports

1063-7745 (ISSN) 1562-689X (eISSN)

Vol. 58 5 735-738

Ämneskategorier

Fysik

DOI

10.1134/s1063774513050143

Mer information

Senast uppdaterat

2019-01-18