Transformation and Release of Potassium, Chlorine, and Sulfur from Wheat Straw under Conditions Relevant to Dual Fluidized Bed Gasification
Artikel i vetenskaplig tidskrift, 2013

The release and transformation of potassium (K), chlorine (Cl), and sulfur (S) from biomass during thermochemical conversion processes may lead to problems, such as the corrosion and fouling of heat transfer surfaces, agglomeration of bed material, and the poisoning of catalysts used in the downstream processes of gasifiers. To predict and to mitigate effectively these problems, information regarding the quantity and mechanism of the release of these elements under relevant operating conditions is required. In the present work, the release of K, Cl, and S from wheat straw under conditions relevant to dual fluidized bed gasification were quantified in a laboratory-scale bubbling fluidized bed reactor. During the pyrolysis step, the bed temperature ranged from 550 to 900 degrees C, while the residence time for the fuel in the reactor was fixed at 3 mm. The char samples obtained from the pyrolysis step were partially combusted at the same temperature at which they were produced for an additional 3 mm. The fractions of the elements released from the fuel were quantified by chemical analysis of the char/residual ash obtained in each experiment and a mass balance across the system. Overall, 75%-62% of the Cl, 59%-67% of the S, and 14%-31% of the K in the virgin wheat straw were released during pyrolysis conducted within the investigated temperature range. The char obtained from the pyrolysis process contained significantly higher amounts of K, Cl, and S than the virgin fuel. Furthermore, the ash content of the char was about 5-fold higher than that of the virgin fuel. This suggests that at combustion-relevant temperatures, complete combustion of the char is more likely to result in severe ash-related problems than combustion of the virgin fuel. Partial combustion of the char resulted in additional release of K, Cl, and S. In addition to the experimental results, the transformation and release of the elements during this process are discussed with the aid of chemical thermodynamic equilibrium modeling and leaching.

THERMAL-CONVERSION

PRODUCT GAS

WOOD COMBUSTION

BURNING

HIGH-TEMPERATURE CORROSION

PART 1

INORGANIC ELEMENTS

BIOMASS FUELS

MIXTURES

GAS-PHASE

FOULING TENDENCY

Författare

Placid Tchoffor Atongka

Chalmers, Energi och miljö, Energiteknik

SP Sveriges Tekniska Forskningsinstitut AB

K. O. Davidsson

SP Sveriges Tekniska Forskningsinstitut AB

Henrik Thunman

Chalmers, Energi och miljö, Energiteknik

Energy & Fuels

0887-0624 (ISSN) 1520-5029 (eISSN)

Vol. 27 12 7510-7520

Ämneskategorier

Energiteknik

Styrkeområden

Energi

DOI

10.1021/ef401703a

Mer information

Senast uppdaterat

2022-08-11