Effect of TiO2 nano-filler and EC plasticizer on electrical and thermal properties of poly(ethylene oxide) (PEO) based solid polymer electrolytes
Artikel i vetenskaplig tidskrift, 2014

Ionic conductivity of poly(ethylene oxide)-lithium trifluoromethanesulfonate (LiCF3SO3 or LiTf) based polymer electrolyte has been increased by incorporating TiO2 nano-filler. Incorporation of 10 wt.% TiO2 exhibited the highest conductivity enhancement with a value of 4.9 x 10(-5) S cm(-1) at 30 degrees C. A further enhancement in conductivity to a value of 1.6 x 10(-4)S cm(-1) at 30 degrees C has been obtained by the incorporation of 50 wt.% ethylene carbonate (EC) plasticizer. Both additives cause a reduction of the PEO crystalline phase content and an increased segmental flexibility leading to conductivity enhancement.

Plasticizers

Nano-composite polymer electrolytes

Ionic conductivity enhancement

TiO2 nano-fillers

Författare

K. Vignarooban

University of Peradeniya

M. A. K. L. Dissanayake

University of Peradeniya

Ingvar Albinsson

Göteborgs universitet

Bengt-Erik Mellander

Chalmers, Teknisk fysik, Nukleär teknik

Solid State Ionics

0167-2738 (ISSN)

Vol. 266 25-28

Drivkrafter

Hållbar utveckling

Styrkeområden

Nanovetenskap och nanoteknik

Energi

Materialvetenskap

Ämneskategorier

Nanoteknik

Den kondenserade materiens fysik

DOI

10.1016/j.ssi.2014.08.002

Mer information

Skapat

2017-10-07