Crystallographic and Magnetic Properties of the Spinel-type Ferrites ZnxCo1-xFe2O4 (0.0 <= x <= 0.75)
Paper i proceeding, 2015

Ultrahigh frequencies (UHF) have applications in signal and power electronics to minimize product sizes, increase production quantity and lower manufacturing cost. In the UHF range of 300 MHz to 3 GHz, ferrimagnetic iron oxides (ferrites) are especially useful because they combine the properties of a magnetic material with that of an electrical insulator. Ferrites have much higher electrical resistivity than metallic ferromagnetic materials, resulting in minimization of the eddy current losses, and total penetration of the electromagnetic (EM) field. Hence ferrites are frequently applied as circuit elements, magnetic storage media like read/write heads, phase shifters and Faraday rotators. The electromagnetic properties of ferrites are affected by operating conditions such as field strength, temperature and frequency. The spinel system ZnxCo1-xFe2O4 (x= 0.0, 0.25, 0.50 and 0.75) has been prepared by the standard solid state sintering method. X-ray and neutron powder diffraction measurements were performed at room temperature. Neutron diffraction data analysis confirms the cubic symmetry corresponding to the space group Fd3m. The distribution of three cations Zn2+, Co2+ and Fe3+ over the spinel lattice and other crystallographic parameters like lattice constant, oxygen position parameter, overall temperature factor and occupancies of different ions in different lattice sites for the samples have been determined from the analysis of neutron diffraction data. The lattice constant increases with increasing Zn content in the system. The magnetic structure was found to be ferrimagnetic for the samples with x <= 0.50. Magnetization measurements show that with the increase of Zn content in the system the value of saturation magnetization first increases and then decreases. The variation of the magnetic moment with Zn substitution has been discussed in terms of the distribution of magnetic and non-magnetic ions over the A and B sub-lattices and their exchange coupling.

neutron diffraction

Ferrites

magnetic measurements

structural characterization

Författare

A. K. Azad

Universiti Brunei Darussalam

A. K. M. Zakaria

Bangladesh Atomic Energy Commission

M. Y. Jewel

Jahangirnagar University

A. Khan

Jahangirnagar University

S. M. Yunus

Bangladesh Atomic Energy Commission

I. Kamal

Bangladesh Atomic Energy Commission

T. K. Datta

Bangladesh Atomic Energy Commission

Sten Eriksson

Chalmers, Kemi och kemiteknik, Energi och material

AIP Conference Proceedings

0094-243X (ISSN) 1551-7616 (eISSN)

Vol. 1660 090050
9780735413047 (ISBN)

Ämneskategorier

Matematik

Fysik

DOI

10.1063/1.4926639

ISBN

9780735413047

Mer information

Skapat

2017-10-08