Colossal magneto-resistance effect in epitaxially grown La2/3Ca1/3Mno3 perovskite-like manganite thin films
Artikel i vetenskaplig tidskrift, 2005

We report in this work, study on colossal magnetoresistance (CMR) effect in epitaxial La2/3Ca1/3 MnO3 thin films grown on SrTiO3 (0 0 1) substrates by pulsed laser deposition (PLD) technique. The films were grown on as-received SrTiO3 substrates and on SrTiO3 substrates prepared by HF etching (Koster et al., Appl. Phys. Lett. 73 (1998) 2920; V. Leca et al., Wet etching methods for perovskite substrates, University of Twente, MESA+ Research Institute, Low Temperature Division). Two of the samples were annealed in different conditions to investigate the films heat treatment effect on electric and magnetic properties. Electrical resistance was done using the four-probe method at temperatures in the range of 2–375 K without a magnetic field and in an external field of 5 T applied in the film plane. Resistance-magnetic field (R vs. H) at 77 K for the two annealed samples was done in a 5 T sweep magnetic field. The surface morphology and structural information of the films were obtained using atomic force microscopy (AFM) and X-ray diffraction (XRD), respectively. Secondary ion mass spectroscopy (SIMS) analysis was performed on the annealed samples to investigate any possible chemical reaction between La2/3Ca1/3MnO3 thin films and SrTiO3 substrate.

Författare

Anayesu Malisa

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Zdravko Ivanov

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Journal of Magnetism and Magnetic Materials

0304-8853 (ISSN)

Vol. 295 3 277-283

Ämneskategorier

Materialteknik

DOI

10.1016/j.jmmm.2005.01.030

Mer information

Skapat

2017-10-08