Understanding the mechanism of low temperature deactivation of Cu/SAPO-34 exposed to various amounts of water vapor in the NH3-SCR reaction
Journal article, 2019

The low temperature hydrothermal stability of Cu/SAPO-34 catalysts for the NH3-SCR reaction, prepared by three different structure directing agents (SDAs), i.e., morpholine (MO), triethylamine (TEA), and tetraethylammonium hydroxide (TEAOH), was investigated by exposing them to various amounts of water vapor. XRD and BET studies indicate that there was no sign of Cu/SAPO-34 catalyst's chabazite (CHA) structural collapse due to water vapor exposure up to 55 h regardless of SDA choice. However, a multinuclear solid-state magic angle spinning (SS-MAS) NMR study of Cu/SAPO-34(MO, TEA, TEAOH) suggests that the water vapor exposure had significantly altered the coordination environment of Al, P, and Si, the extent of which depends on the choice of SDA along with water vapor exposure time. NO-DRIFTS and H-2-TPR studies suggest different mobility for Cu ions between the 6MR and 8MR of the CHA structure in Cu/SAPO-34(MO, TEA, TEAOH) as the result of water vapor exposure and during the NH3-SCR reaction. The mechanisms for low temperature deactivation of Cu/SAPO-34 were proposed as follows: 1) irreversible Si condensation in the support and 2) Cu migration to less accessible sites and/or formation of CuOx clusters depending on Cu mobility.

Author

Jung Won Woo

Chalmers, Chemistry and Chemical Engineering, Chemical Technology

Diana Bernin

Chalmers, Chemistry and Chemical Engineering, Chemical Technology

Homayoun Ahari

FCA US LLC

Mark Shost

FCA US LLC

Michael Zammit

FCA US LLC

Louise Olsson

Chalmers, Chemistry and Chemical Engineering, Chemical Technology

Catalysis Science and Technology

2044-4753 (ISSN) 2044-4761 (eISSN)

Vol. 9 14 3623-3636

Subject Categories

Chemical Engineering

DOI

10.1039/c9cy00240e

More information

Latest update

2/8/2021 5