High temperature oxidation behavior of DMLs produced inconel 625
Paper in proceeding, 2020

This work presents a study of the high temperature oxidation behavior of Inconel 625 (IN625) processed by direct metal laser sintering (DMLS). IN625 is a Nickel-based superalloy characterized by outstanding high temperature oxidation and corrosion resistance. However, taking into account that DMLS produced IN625 has significantly different microstructure and surface properties than the conventional produced IN625, it is important to evaluate the potential change in the oxidation behavior of this alloy, not reported in literature yet. In this study a complete characterization of the oxidation behavior of DMLS fabricated IN625, in as-built and solutionized (1150°C/2h) conditions, was performed at 900°C for 8, 24, 48, 72 and 96 hours in air. Oxidized samples were characterized utilizing advanced microscopy and surface analysis techniques (SEM+EDX, XPS). Results indicate that oxide formed is mainly composed of Cr2O3. Oxidation stabilizes after around 24 hours, indicating good corrosion resistance of the DMLS produced IN625.


Simone Parizia

Polytechnic University of Turin

Istituto Italiano di Tecnologia

Giulio Marchese

Polytechnic University of Turin

Masoud Rashidi

Chalmers, Industrial and Materials Science, Materials and manufacture

Gloria Basile

Polytechnic University of Turin

Sara Biamino

Polytechnic University of Turin

Diego Manfredi

Istituto Italiano di Tecnologia

Eduard Hryha

Chalmers, Industrial and Materials Science, Materials and manufacture

Euro PM 2018 Congress and Exhibition

9781899072507 (ISBN)

European Powder Metallurgy Congress and Exhibition, Euro PM 2018
Bilbao, Spain,

Subject Categories


Other Chemistry Topics

Corrosion Engineering

More information

Latest update

1/5/2021 7