Continuous Microfluidic Synthesis of Pd Nanocubes and PdPt Core–Shell Nanoparticles and Their Catalysis of NO2 Reduction
Journal article, 2019

Faceted colloidal nanoparticles are currently of immense interest due to their unique electronic, optical, and catalytic properties. However, continuous flow synthesis that enables rapid formation of faceted nanoparticles of single or multi-elemental composition is not trivial. We present a continuous flow synthesis route for the synthesis of uniformly sized Pd nanocubes and PdPt core-shell nanoparticles in a single-phase microfluidic reactor, which enables rapid formation of shaped nanoparticles with a reaction time of 3 min. The PdPt core-shell nanoparticles feature a dendritic, high surface area with the Pt shell covering the Pd core, as verified using high-resolution scanning transmission electron microscopy and energy dispersive X-ray spectroscopy. The Pd nanocubes and PdPt core-shell particles are catalytically tested during NO2 reduction in the presence of H2 in a flow pocket reactor. The Pd nanocubes exhibited low-temperature activity (i.e., <136 °C) and poor selectivity performance toward production of N2O or N2, whereas PdPt core-shell nanoparticles showed higher activity and were found to achieve better selectivity during NO2 reduction retaining its basic structure at relatively elevated temperatures, making the PdPt core-shell particles a unique, desirable synergic catalyst material for potential use in NOx abatement processes.

flow chemistry






Anna Pekkari

Chalmers, Chemistry and Chemical Engineering, Applied Chemistry

Zafer Say

Chalmers, Physics, Chemical Physics

Arturo Susarrey- Arce

Chalmers, Physics, Chemical Physics

Christoph Langhammer

Chalmers, Physics, Chemical Physics

Hanna Härelind

Chalmers, Chemistry and Chemical Engineering, Applied Chemistry

Victor Sebastian

University of Zaragoza

CIBER Bioingenieria, Biomateriales y Nanomedicina

Kasper Moth-Poulsen

Chalmers, Chemistry and Chemical Engineering, Applied Chemistry

ACS Applied Materials & Interfaces

1944-8244 (ISSN) 1944-8252 (eISSN)

Vol. 11 39 36196-36204

Subject Categories

Inorganic Chemistry

Materials Chemistry

Other Physics Topics



More information

Latest update

4/6/2022 5