The role of Pd-Pt Interactions in the Oxidation and Sulfur Resistance of Bimetallic Pd-Pt/γ-Al2O3 Diesel Oxidation Catalysts

Journal article, 2021

Diesel oxidation catalysts (DOC) were investigated for oxidation activity, NO conversion stability, and sulfur poisoning/regeneration on Pd/Al2O3, Pt/Al2O3, and Pd-Pt/Al2O3 catalysts. The Pd/Al2O3 catalyst was more active for CO and hydrocarbon (C3H6 and C3H8) oxidation, while the Pt/Al2O3 catalyst efficiently oxidized NO. The formation of a Pd-Pt alloy in the Pd-Pt/Al2O3 catalyst maintained Pd in a more reduced phase, resulting in the superior activity of this catalyst for the oxidation of CO, C3H6, and NO in comparison with its monometallic counterparts. The Pd-Pt alloy not only provided more low-temperature activity but also retained the stability of NO oxidation. The Pd-Pt alloy also favored the spillover of SO2 to the alumina support, resulting in significantly higher adsorption capacity of the Pd-Pt/Al2O3 catalyst, extensively prolonging its lifetime. However, the stable sulfates on Pd-Pt/Al2O3 made it difficult to completely regenerate the catalyst. The bimetallic sample showed higher activity for CO, C3H8, and C3H6 after sulfur poisoning and regeneration.