Texture of Electrodeposited Nanocrystalline Ni-Fe with banded structure
Artikel i vetenskaplig tidskrift, 2012

Optical microscopy on the etched cross-section of a nanocrystalline Ni-18 wt.% Fe electrodeposit revealed the existence of a banded structure perpendicular to the growth direction. To evaluate if the banded structure is affecting grain growth and texture development, EBSD orientation maps were obtained after annealing for 30 min at 300, 350, and 400°C. Grown grains were found to be random in shape and no preferential sites for grain growth were observed. The texture of the grown grains is changing upon annealing and the final <111> fibre texture parallel to growth direction of the electrodeposit can be obtained from texture components found at lower annealing temperatures when performing one or two consecutive twinning operations.

nanocrystalline material

annealing

electroplating

Ni-Fe

EBSD

banded structure

Författare

Uta Klement

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Mehrdad Shahabi Navid

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Glenn Hibbard

Materials Science Forum

0255-5476 (ISSN)

Vol. 702-703 912-915

Ämneskategorier

Materialteknik

Styrkeområden

Materialvetenskap

DOI

10.4028/www.scientific.net/MSF.702-703.912

Mer information

Skapat

2017-10-07