Cobalt (II) Chloride Promoted Formation of Honeycomb Patterned Cellulose Acetate Films
Artikel i vetenskaplig tidskrift, 2012

CoCl2 containing honeycomb patterned films were prepared from cellulose acetate (CA)/CoCl2/acetone solutions by the breath figure method in a wide range of humidities. Size and pore regularity depend on the CA/CoCl2 molar ratio and humidity. When replacing CoCl2 with Co(NO3)2 or CoBr2, no formation of ordered porosity in the cellulose acetate films is observed. According to data from scanning electron microscopy (SEM), Energy Dispersive X-ray Microanalysis (EDX), X-ray Diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy, the key role in the formation of honeycomb structures can be attributed to the physical and chemical properties of CoCl2 – hygroscopicity, low interaction with CA, and extraction from CA/CoCl2/acetone solution by water droplets condensed on the surface of the CA/CoCl2 solution. Obtained films are prospective for using in catalysis, hydrogen fuel cells, and optical sensing materials.

Cobalt (II) chloride

Cellulose acetate

Honeycomb patterned film

Breath figure method

Författare

Olga Naboka

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

Anke Sanz-Velasco

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

Per Lundgren

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

Peter Enoksson

Chalmers, Mikroteknologi och nanovetenskap (MC2), Elektronikmaterial och system

Wallenberg Wood Science Center (WWSC)

Paul Gatenholm

Wallenberg Wood Science Center (WWSC)

Chalmers, Kemi- och bioteknik, Polymerteknologi

Journal of Colloid and Interface Science

0021-9797 (ISSN)

Vol. 367 485-493

Ämneskategorier

Materialteknik

Kemi

Styrkeområden

Transport

Produktion

Materialvetenskap

DOI

10.1016/j.jcis.2011.10.030

PubMed

22074692