Ni/C/SiO2 nanostructured composites synthesized by carbonization of carboxymethyl cellulose
Paper i proceeding, 2012

Ni/C/SiO2 porous composites were synthesized by one-pot approach by carbonization of sodium carboxymethyl cellulose/SiO2 xerogels containing NiCl2. Synthesized composites are mesoporous materials (average pore size 11.8 -15.1 nm) with the surface area 72.1 – 91.1 m2. Ni nanoparticles of 30-90 nm in diameter are evenly distributed within the volume of composites. The hydrogen sorption capacity at -196°C and 20 bar measured for as-synthesized samples was up to 0,32%.

hydrogen sorption

carbonization

porous composites

Visa alla personer

Publicerad i

ECCM 15 - 15th European Conference On Composite Materials, 24-28 June 2012, Venice, Italy, paper 1052 (1-7).

Vol. 367 Nummer/häfte 1 s. 485-493

Kategorisering

Drivkrafter

Hållbar utveckling

Styrkeområden

Nanovetenskap och nanoteknik

Transport

Produktion

Energi

Materialvetenskap

Ämneskategorier (SSIF 2011)

Fysik

Naturresursteknik

Nanoteknik

Kemi

Infrastruktur

Myfab (inkl. Nanotekniklaboratoriet)

Identifikatorer

Mer information

Senast uppdaterat

2025-03-10

Feedback och support

Om du har frågor, behöver hjälp, hittar en bugg eller vill ge feedback kan du göra det här nedan. Du når oss också direkt per e-post research.lib@chalmers.se.

Om tjänsten

Research.chalmers.se innehåller information om forskning på Chalmers, publikationer och projekt inklusive information om finansiärer och samarbetspartners.

Läs mer om tjänsten, täckningsgrad och vilka som kan se informationen

Personuppgifter och cookies

Tillgänglighet

Citation Style Language
citeproc-js (Frank Bennett)

Länkar

Chalmers bibliotek
Chalmers forskning
Chalmers examensarbeten

Chalmers tekniska högskola

412 96 GÖTEBORG
TELEFON: 031-772 10 00
WWW.CHALMERS.SE