Influence of high temperature hold times on the fatigue crack propagation in Inconel 718
Artikel i vetenskaplig tidskrift, 2011

High temperature fatigue crack growth in Inconel 718 has been studied at the temperatures 450 °C, 500 °C, 550 °C and 650 °C. The tests were conducted both without hold times and with hold times of different lengths and with a mix of both. Focus has been on quantifying the effect the hold time has upon the crack growth rate and how much it damages the material. Furthermore, it has been investigated how this damage influences the actual cracking behavior, i.e. where in the loading cycle the damage contributes most to the crack growth. This damage is related to the concept of a damaged zone in front of the crack tip. The size of the damaged zone has been derived from the tests and a microscopy study to confirm the findings has also been carried out. It is found that the concept of a damaged zone can be a successful explanatory model for the observed crack growth behavior under high temperature hold time. © 2011 Elsevier Ltd. All rights reserved.

Grain boundary embrittlement

Nickel-base superalloys

Fatigue crack propagation

Inconel 718

Hold times

Författare

David Gustafsson

J.J. Moverare

S.A.H. Johansson

K. Simonsson

Magnus Hörnqvist Colliander

T. Mnsson

S. Sjöström

International Journal of Fatigue

0142-1123 (ISSN)

Vol. 33 1461-1469

Ämneskategorier

Maskinteknik

Materialteknik

Annan materialteknik

DOI

10.1016/j.ijfatigue.2011.05.011